NCM111 Cathode Sheet on Aluminum Foil (Single / Double-Sided Coating)

Name: NCM111 Cathode Sheet on Aluminum Foil (Single / Double-Sided Coating)

Material Type: NCM111 (NMC111, Ni:Co:Mn = 1:1:1) on 16 μm Aluminum Foil

Product Code: XN-NCM111-ES

Product Introduction:

NCM111 (also known as NMC111 or NMC333) is a balanced lithium nickel cobalt manganese oxide cathode with equal molar ratios of Ni, Co, and Mn (1:1:1). The electrode sheet is coated on 16 μm aluminum foil and available in both single-sided (13 ± 0.20 mg/cm²) and double-sided (26 ± 0.4 mg/cm²) configurations. Electrode size is 241 mm × 200 mm with a 12.5 mm uncoated edge on each side. Reference specific capacity is 150 mAh/g at 0.1C (2.8–4.25 V). Supplied 5 pcs/bag.

Key Features:

NCM111 (Ni:Co:Mn = 1:1:1) — balanced capacity and stability
Reference specific capacity 150 mAh/g at 0.1C (2.8–4.25 V)
Available in single-sided (13 ± 0.20 mg/cm²) and double-sided (26 ± 0.4 mg/cm²) coating
Current collector: 16 μm aluminum foil, 4.22 mg/cm²
Compacted density: 3.0 ± 0.1 g/cm³ (single-sided) / 3.4 ± 0.1 g/cm³ (double-sided)
Active material mass ratio 95.5%
Electrode size: 241 × 200 mm (coating area 241 × 175 mm, 12.5 mm uncoated edges on each side)
Packaging: 5 pcs/bag

Single-Sided Coating Specifications:

Double-Sided Coating Specifications:

Notes:

1. The active material mass ratio is based on actual measurement; the above parameters are calculated from theoretical active material data.
2. After opening, please seal and store properly. It can be kept in a glove box or in an oven at 60°C.

Storage & Handling:

Store sealed in a cool, dry, low-humidity environment. After opening, reseal immediately and store in a glove box or in a drying oven at 60°C. Handle by the edges to avoid contaminating the active coating.

Note: Specifications are for reference only. Actual electrochemical performance depends on counter/reference electrode selection, electrolyte, separator, cell assembly conditions, and cycling protocol. For anode electrode sheets, see the Anode Materials category. For electrolytes, see the Electrolytes category. For coin cell assembly components, see Coin Cells & Hardware.