Aqueous Binder LA136D for silicon-carbon anodes

Aqueous Binder, LA136D

SKU: LA-136D

Aqueous Binder, LA136D is an aqueous battery binder. Documented specifications include 10000-18000 mPa·s viscosity at 40°C, ≤1.0 μm D50, 6.0 ± 0.2% solid content and pH 6.5-9.

Need formulation guidance or a research quotation? Request a competitive quote today!

Aqueous Binder, LA136D

Product Type: Aqueous Battery Binder
Product Code: LA-136D

Product Introduction

LA136D is an aqueous solution of an acrylic-acid-derivative multipolymer. The supplied information describes good thermal and electrochemical stability, electrolyte resistance and lower swelling than traditional aqueous anode binders.

Core Features

  • Aqueous acrylic-acid-derivative multipolymer solution
  • Documented viscosity of 10000-18000 mPa·s at 40°C
  • Documented solid content of 6.0 ± 0.2%
  • D50 particle size of ≤1.0 μm
  • Documented electrolyte resistance and low swelling
  • Intended for silicon-carbon and advanced carbon anodes

Technical Specifications

Parameter Specification
Product Code LA-136D
Product Type Aqueous binder
Polymer Description Aqueous solution of an acrylic-acid-derivative multipolymer
Viscosity at 40°C 10000-18000 mPa·s
D50 Particle Size ≤1.0 μm
Solid Content 6.0 ± 0.2%
pH 6.5-9
Appearance Light-yellow transparent viscous solution
Documented Anode Binder Use 1.5-2.5%
Documented Recommended Combination 0.5% CMC + 1.5% LA136D

Applications

  • Silicon-carbon anode slurry formulation
  • Advanced carbon anode material bonding
  • Lithium-ion battery electrode research
  • Electrolyte-resistance and binder-swelling studies

Note: The supplied guidance lists 1.5-2.5% LA136D in anode slurry and a recommended combination of 0.5% CMC + 1.5% LA136D. Confirm the formulation basis and optimize the ratio for the selected material and process. Browse the Binders category for related products.