Xinxiang Tianli TLM510 NCM Cathode Material 1kg

Name: Xinxiang Tianli TLM510 NCM Cathode Material

Material Type: Lithium Nickel Cobalt Manganese Oxide (NCM) Ternary Cathode Material

Product Code: TLM510

Brand: Xinxiang Tianli

Product Introduction:

The Xinxiang Tianli TLM510 is a lithium nickel cobalt manganese oxide (NCM) ternary cathode material supplied as a uniform spherical / quasi-spherical powder. The material has D50 11.5 ± 2.5 μm, tap density ≥ 2.20 g/cm³, BET specific surface area 0.20–0.60 m²/g, and total Ni+Co+Mn content ≥ 58.00 wt%. XRD confirms phase purity matching the ICSD standard (82-0340) with no impurity phase peaks.

Key Features:

NCM ternary cathode chemistry — Ni+Co+Mn total content ≥ 58.00 wt%
First-cycle discharge capacity 162.35 mAh/g at 0.1C, 2.75–4.25 V (half cell)
First-cycle efficiency 87.91%
Particle size distribution — D10 ≥ 5.00 μm / D50 11.5 ± 2.5 μm / D90 ≤ 25.00 μm
High tap density ≥ 2.20 g/cm³ supports high electrode loading
BET specific surface area 0.20–0.60 m²/g
Low moisture content ≤ 0.05 wt%
Low impurity content — Fe ≤ 0.0100 wt%, Cu ≤ 0.0050 wt%, Ca/Mg/Na ≤ 0.0300 wt%
Uniform spherical / quasi-spherical particle morphology (by SEM)
XRD pattern matches ICSD standard 82-0340 with no impurity phase peaks

Chemical Composition:

Physical Properties:

Particle size distribution curve:

SEM Morphology:

SEM imaging (×3000) confirms uniform spherical / quasi-spherical secondary-particle morphology.

XRD Pattern:

The XRD pattern matches the ICSD standard 82-0340 with no impurity phase peaks.

Electrochemical Performance (Lithium-Metal Coin Half-Cell, 0.1C, 2.75–4.25 V):

Values measured by Xnergy. Typical values for reference; not guaranteed unless otherwise specified.

Note: Specifications listed above are typical and for reference only. Actual electrochemical performance depends on the specific cell architecture, electrolyte formulation, binder/conductive-additive composition, coating thickness, calendering parameters, formation protocol, and testing conditions. For complete lithium-ion battery electrode preparation workflows, see also Xnergy’s related products in the Cathode Materials category, Anode Materials category, Binders category, and Current Collectors category. For electrode-coating equipment, see the Coating equipment category including Automatic Film Coater XN-VC-300, XN-VCH-300, and Slot-Die Coating System XN-SDC. For electrode calendering, see the Calendering equipment category. For mixing and drying, see Planetary Vacuum Mixer and Three-Door Vacuum Drying Oven (XN-DVO-3). For other NCM ternary cathode materials in our catalog, see also Zhenhua E-Chem Single-Crystal NCM523 Cathode, Zhenhua E-Chem NCM613 Cathode, Ronbay S760 Polycrystalline NCM613 Cathode, BTR M9-FC Polycrystalline NCM Cathode, and Shanshan T31D NCM Cathode Material.