Ronbay SC60 Single-Crystal NCM Cathode Material 1kg

Name: Ronbay SC60 Single-Crystal NCM Cathode

Material Type: Single-Crystal Lithium Nickel Cobalt Manganese Oxide (NCM)

Product Code: SC60

Brand: Ronbay

Product Introduction:

The Ronbay SC60 is a single-crystal lithium nickel cobalt manganese oxide (NCM) cathode material with Ni 35-39 wt%, Co 4-7 wt%, and Mn 14-17 wt%. The material is supplied as a black powder with D50 3.00-5.00 μm, tap density ≥ 2.00 g/cm³, and specific surface area ≤ 1.00 m²/g. SEM confirms single-crystal microstructure, and the material is graded A in dry 325-mesh sieving.

Key Features:

Single-crystal NCM chemistry — Ni 35-39 / Co 4-7 / Mn 14-17 wt%
Half-cell capacity ≥ 185 mAh/g at 0.1C, 3.0–4.4 V (25 ± 2°C)
First-cycle efficiency ≥ 85%
Particle size distribution — D10 ≥ 1.00 μm / D50 3.00-5.00 μm / D90 ≤ 15.00 μm
High tap density ≥ 2.00 g/cm³
Low specific surface area ≤ 1.00 m²/g
Low surface lithium residues — CO₃²⁻ < 0.30 wt%, OH⁻ < 0.20 wt%, Free Li⁺ ≤ 0.10 wt%
Low impurity content — Fe, Ca, Zn, Na, Cu all well below specification limits
Low magnetic impurities (Fe + 1.5Cr + Zn) ≤ 100 ppb
Grade A sieving (100% pass 325 mesh)
RoHS compliant (EU standards)

Chemical Composition:

Impurities & Surface Lithium Residues:

Particle Size Distribution (PSD):

Particle size distribution curve:

Physical Properties:

SEM Morphology:

SEM imaging confirms well-developed single-crystal particle morphology with smooth facets and a uniform particle size distribution.

SEM at low magnification (20 μm scale bar):

SEM at high magnification (10 μm scale bar):

XRD Pattern:

Electrochemical Performance (Half-Cell, 0.1C, 3.0–4.4 V, 25 ± 2°C):

Values measured by Xnergy. Typical values for reference; not guaranteed unless otherwise specified.

Packaging:

Vacuum-sealed in aluminum-foil bag, with an outer PE plastic bag to prevent corrosion and contamination. Bags are placed in grey plastic drums or cardboard boxes, with each drum / box containing 20.00–20.02 kg net weight of material.

Storage:

Store sealed in a cool, dry place. Shelf life: 1 year from the production date.

Note: Specifications listed above are typical and for reference only. Actual electrochemical performance depends on the specific cell architecture, electrolyte formulation, binder/conductive-additive composition, coating thickness, calendering parameters, formation protocol, and testing conditions. For complete lithium-ion battery electrode preparation workflows, see also Xnergy’s related products in the Cathode Materials category, Anode Materials category, Binders category, and Current Collectors category. For electrode-coating equipment, see the Coating equipment category including Automatic Film Coater XN-VC-300, XN-VCH-300, and Slot-Die Coating System XN-SDC. For electrode calendering, see the Calendering equipment category. For mixing and drying, see Planetary Vacuum Mixer and Three-Door Vacuum Drying Oven (XN-DVO-3). For other Ronbay single-crystal NCM cathodes, see also Xnergy’s Ronbay S740B Single-Crystal NCM Cathode. For comparison with single-crystal NCM from other suppliers, see Zhenhua E-Chem Single-Crystal NCM523 Cathode, BTR M2-S Single-Crystal Ni83 NCM Cathode, and EASPRING ME-93SC Single-Crystal NCM Cathode.